Solid ground curing
Solid ground curing (SGC) is a photo-polymer-based additive manufacturing (or 3D printing)[1] technology used for producing models, prototypes, patterns, and production parts, in which the production of the layer geometry is carried out by means of a high-powered UV lamp through a mask. As the basis of solid ground curing is the exposure of each layer of the model by means of a lamp through a mask, the processing time for the generation of a layer is independent of the complexity of the layer.[2] SGC was developed and commercialized by Cubital Ltd. of Israel in 1986[3] in the alternative name of Solider System.
While the method offered good accuracy and a very high fabrication rate, it suffered from high acquisition and operating costs due to system complexity. This led to poor market acceptance and systems are no longer being sold. [4] Objet Geometries of Israel retained intellectual property of the process after the closure of Cubital Ltd. in 2002,[5]
The SGC process involved hardening photopolymers by exposing the entire surface to UV light using masks. Each layer of the prototype was simultaneously cured by the UV lamp, eliminating the need for post-curing processes. The key steps in SGC include calculating the cross-section of each layer, generating an optical mask, applying a thin layer of liquid photopolymer, and exposing it to UV light. Residual liquid is removed, voids are filled with melted wax, and the layer is trimmed to the desired thickness. This process is repeated until the final layer is processed, after which the wax is melted away to reveal the completed part.
The primary advantage of SGC is that it does not require support structures, as wax is used to fill voids, resulting in highly accurate products. Models produced by SGC are particularly accurate in the Z-direction due to the milling step after each light exposure. However, the technology generates significant waste and has high operating costs, which have contributed to its decline in use.
Technology
![](http://upload.wikimedia.org/wikipedia/commons/thumb/b/b6/Schematic_Diagram_of_Solid_Ground_Curing_Process.jpg/220px-Schematic_Diagram_of_Solid_Ground_Curing_Process.jpg)
Solid ground curing utilizes the general process of hardening of photopolymers by a complete lighting and hardening of the entire surface, using specially prepared masks.[6] In SGC process, each layer of the prototype is cured by exposing to an ultra violet (UV) lamp instead of by laser scanning. So that, every portion in a layer are simultaneously cured and do not require any post-curing processes. The process contains the following steps.[7]
- The cross section of each slice layer is calculated based on the geometric model of the part and the desired layer thickness.
- The optical mask is generated conforming to each cross section.
- After leveling, the platform is covered with a thin layer of liquid photopolymer.
- The mask corresponding to the current layer is positioned over the surface of the liquid resin, and the resin is exposed to a high-power UV lamp.
- The residual liquid is removed from the workpiece by an aerodynamic wiper.
- A layer of melted wax is spread over the workpiece to fill voids. The wax is then solidified by applying a cold plate to it.
- The layer surface is trimmed to the desired thickness by a milling disk.
- The current workpiece is covered with a thin layer of liquid polymer and step 4 to 7 are repeated for each succeeding upper layer until the topmost layer has been processed.
- The wax is melted away upon completion of the part.
Advantages and disadvantages
The primary advantage of the solid ground curing system is that it does not require a support structure since wax is used to fill the voids, highly accurate products can be obtained.[8] The model produced by SGC process is comparatively accurate in the Z-direction because the layer is milled after each light-exposure process.[9] Although it offers good accuracy coupled with high throughput, it produces too much waste and its operating costs are comparatively high due to system complexity.[10]
References
- ^ The engineer: The rise of additive manufacturing(n.d.). Retrieved from
- ^ Gebhardt, I.A.(2003). Rapid Prototyping: Industrial Rapid Prototyping System: Prototyper: Solid Ground Curing – Cubital. (pp. 105-109)
- ^ Solid Ground Curing(n.d.). Retrieved from
- ^ Castle Island Co.. (2002, June 22). Solid Ground Curing. Retrieved from Archived 2004-10-30 at the Wayback Machine
- ^ Gebhardt, I.A.(2003). Rapid Prototyping: Industrial Rapid Prototyping System: Prototyper: Solid Ground Curing – Cubital. (pp. 105-109)
- ^ Rapid Prototyping: Rapid Ground Curing(n.d.). Retrieved from
- ^ Lee, K.W. (1999). Principles of CAD/CAM/CAE Systems: Rapid Prototyping and Manufacturing: Solid Ground Curing (pp. 383-384).
- ^ Dolenc, A.(1994).An Overview Of Rapid Prototyping Technologies In Manufacturing:Solid Ground Curing. (p. 8)
- ^ Gebhardt, I.A.(2003). Rapid Prototyping: Industrial Rapid Prototyping System: Prototyper: Solid Ground Curing – Cubital. (pp. 105-109)
- ^ Rapid Ground Curing: An Introduction(n.d.). Retrieved from
- v
- t
- e
- Stereolithography
- Computed axial lithography
- Continuous liquid interface production
- Solid ground curing
- Fused filament fabrication
- Robocasting
- EAM of metals and ceramics
- Powder bed and inkjet head 3D printing
- Electron beam melting
- Selective heat sintering
- Selective laser melting
- Selective laser sintering
- Laminated object manufacturing
- Ultrasonic consolidation